| Customization: | Available |
|---|---|
| Application: | Electrical Power System, Electronic Device, Industrial Equipment |
| Material: | Wood |
|
Still deciding? Get samples of US$ 15/Piece
Order Sample
|
| Shipping Cost: | Contact the supplier about freight and estimated delivery time. |
|---|
| Payment Methods: |
|
|---|---|
| Support payments in USD |
| Secure payments: | Every payment you make on Made-in-China.com is protected by the platform. |
|---|
| Refund policy: | Claim a refund if your order doesn't ship, is missing, or arrives with product issues. |
|---|
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
The electrical laminated wood provided by Weshare uses high-quality insulation materials and has excellent electrical insulation properties. It can effectively insulate, maintain stable physical properties in high temperature environments, and can effectively prevent material deformation or expansion under extreme working conditions, extending The service life of the equipment.
Weshare understands that each customer's application scenarios and needs are different, so we provide comprehensive customized services. From size and thickness to specific properties (such as temperature resistance, chemical resistance, etc.), packaging (cartons, wooden boxes, pallets, etc.), we can precisely customize it according to your specific requirements to ensure that the electrical laminated wood for each project is perfect. Perfectly matched to your work environment and technology needs.
| Normal Thickness | Distance of points on the veneer face from light weight straight ruler | |
| 500 straight ruler | 11000straight ruler | |
| ≤15 | 2 | 4 |
| >15...≤25 | 1.5 | 3 |
| >25...≤60 | 1 | 2 |
| >60 | 1 | 1 |
| Capability | Unit | Model | |||||||||
| Veneers technique target | Rings technique target | ||||||||||
| P3B | C1B | C2B | C3B | C4B | T2B | T4B | |||||
| Appearance Density | g/cm³ | 1.1-1.2 | 0.7-0.9 | 0.9-1.1 | 1.1-1.2 | 1.2-1.3 | 0.9-1.1 | 1.2-1.3 | |||
| Moisture | % | ≤6 | ≤6 | ≤6 | ≤6 | ≤6 | ≤6 | ≤6 | |||
| Vertical Layer Direction Flexural Strength |
Direction A | MPa | ≥150 | ≥45 | ≥55 | ≥65 | ≥80 | Diameter>1000mm | ≥100 | ≥140 | |
| Direction B | Diameter≤ 1000mm | ≥90 | ≥125 | ||||||||
| Vertical Layer Direction Flexural Modulus of Elasticity |
Direction A | GPa | ≥14 | ≥4.5 | ≥6 | ≥8 | ≥9 | ≥10 | ≥13 | ||
| Direction B | - | ||||||||||
| Compressibility (Below 20MPa) | C | % | ≤3 | ≤5 | ≤4 | ≤3 | ≤2.5 | ≤5 | ≤4 | ||
| Crev | ≥70 | ≥70 | ≥70 | ≥70 | ≥70 | ≥70 | ≥70 | ||||
| Impact Strength (side Test) | Direction A | KJ/m2 | ≥35 | ≥6 | ≥10 | ≥613 | ≥15 | ≥25 | ≥35 | ||
| Direction B | - | ||||||||||
| Shear Strength | MPa | ≥8 | ≥5 | ≥7 | ≥8 | ≥9 | ≥7 | ≥9 | |||
| Vertical Layer Direction Electric Strength | KV/ | ≥11 | ≥9 | ≥10 | ≥11 | ≥12 | ≥10 | ≥10 | |||
| mm | |||||||||||
| Parallel Layer Direction Puncture Voltage | KV | ≥50 | ≥50 | ≥50 | ≥50 | ≥50 | ≥50 | ≥50 | |||
| Shrinkage After Dried | Direction A | % | ≤0.2 | ≤0.3 | ≤0.3 | ≤0.3 | ≤0.3 | Girth | ≤0.5 | ≤0.5 | |
| Direction B | ≤0.5 | ≤0.3 | ≤0.3 | ≤0.3 | ≤0.3 | ||||||
| Thickness | ≤3 | ≤3 | |||||||||
| Thickness | ≤3 | ≤3 | ≤3 | ≤3 | ≤3 | ||||||
| Oil Absorption | % | ≥8 | ≥8 | ≥15 | ≥8 | ≥50 | ≥15 | ≥5 | |||
| (Δtanδ) Contamination to Liquid Dielectric | - | ≤0.1 | ≤0.1 | ≤0.1 | ≤0.1 | ≤0.1 | ≤0.1 | ≤0.1 | |||